Features

According to EN 1366-4 fire retardant up to 217 min. Ecient seal against smoke and gas. Does not contain CFC’s and H-CFC’s. Excellent adhesion & filling capacity. Excellent mounting capacity and stability. High yield up to 45 liters depending on temperature and humidity. Excellent adhesion on most substrates (except Teflon, PE and PP). High filling capacity. High thermal & acoustical insulation value. After cured, it can be painted, cut, trimmed. No
shrinkage. Mould and water resistant. Conforms to fire class B1 (DIN 4102).

Application Areas

All applications where fire retardant properties are required such as: Installation of door and window frames. Filling and sealing gaps, joints and cavities. Filling of penetrations in walls.Heat insulation of roof construction. Sealing of cable and pipe penetrations. Soundproofing and sealing partition walls. Bonding of insulation materials. Multi-Purpose, adhesion and fixation.

TECHNICAL FEATURES

Basis : Polyurethane Prepolymer
Curing System : Moisture cure
Specific Gravity : 22±3 Kg/cm3 (ASTM D1622)
Tack-Free Time (1 cm width) : 7±3 min (ASTM C1620)
Cutting Time (1cm width) : 30-45 min (ASTM C1620)
Cure-Time : 24 hours
Foam Colour : RED
Yield Volumetric : 40-45L (ASTM C1536)
Post Expansion : 200-250 %
Shrinkage : 0%
Fire Class of the Cured Foam : B1 (DIN 4102)
Thermal Conductivity : 0,036 W/m.k (at 20°C) (DIN 52612)
Compression Strength : 0,03 MPa (DIN 53421)
Water Absorption : Max. 1 vol% (DIN 53428)
Temperature Resistance : -40°C to +90°C
Application Temperature : +5°C to +30°C
Can temperature : +5°C to +30°C