Features

High initial tack. Eco-friendly, free from isocyanate, solvent, acids and halogens. Excellent primerless adhesion to numerous porous and non-porous substrates. Excellent elasticity, no bubble formation, waterproof, no shrinkage, over-paintable. No primer required ( tests recommended). Not lose volume after curing.

Application Areas

It is specially developed as a universal adhesive for bonding various building materials. It is suitable for elastic bonding of panels, profiles and other pieces on the most common substrates such as: stone, concrete, mirrors, glass, plasterboard, PU, PVC, polyester, plastics, enamel, ceramic, copper, lead, zinc, aluminium, metals, R.V.S., wood, HPL and cement fibre panels etc. Common application areas are: Wall cladding elements and ceiling panels. Sound isolation panels (mineral wool, wood-wool cement & plastic foams). Thermal isolation panels (PUR, PIR, PS). Casings and frames in building construction. Wooden and plastic laths, ornaments and frames. Doorsteps, window sills, skirting boards and cover plates. Complete construction elements (such as roofing and facade elements) in frames.

TECHNICAL FEATURES

Chemical Base : AST Polymer
Curing System : Moisture
Density : 1.49 ± 0.03 gr/ml
Appearance/Color : Paste, White, Black or Grey
Tack Free : 15-20 min (23°Cand %50 R.H.)
Curing Rate :Approx. 3,5 mm/ 24hr(23°Cand%50R.H.)
Sagging (ISO 7390) : 0 mm
Shore A Hardness (ISO 868) : 55 ±5
Elongation at Break % (ISO 37) : % 300 / 700
Volume Loss : < -%3 (23°C and %50 R.H.)
Tensile Strength (ISO 37) : 3,0-3,5 N/mm2
Shear Stress : 3121-3237 Pa.
Viscosity (Pa.s) : 3052-3166 Pa.s at 25°C
Viscosity (cps) : 3052000- 3166000 Cps at 25°C
Heat Resistance : -40 o C and +90 o C
Application Temperature : +5 o C and +40 o C